Ọdịdị na akụrụngwa nke polyethylene

Polyethylene (polyethylene, zoro aka na poinmerization nke polymene monomer. Na ụlọ ọrụ, tinyekwara ethylene na ọnụ ọgụgụ pere mpe nke-igwe. Polyethylene na-enweghị isi, na-adịghị egbu egbu, na-adị ka wax, nke nwere ezigbo nguzogide-okpomọkụ (iji okpukpu kporo elu dị ala ruo -100 ~ -70 Celsius C). Ezigbo mmiri na-adịghị mma, n'ihi na polymer molekule site na carbon otu njikọ, nwere ike iguzo ọtụtụ ihe na acid na alkali na alkali (ọ bụghị na-eguzogide ọgwụ oxidizing nke acid). Insosuble na sochiri emechi ụlọ okpomọkụ, mmiri mmiri dị ala, mkpuchi ikuku dị mma.

Ọdịdị na akụrụngwa nke polyethylene

1. Ihe owuwu nke polyethylene

E nwere ike igosipụta ụdị nke polyethylene nke ọ bụla maka nhazi nke polyethylene (Pee) dị ka ndị a:

Ihe mejupụtara ya bụ naanị atọm abụọ nke carbon na hydrogen, na ya nwere ihe dị mfe na obere yinye nke polymer carbon na ogige hydrogen. Ọ bụ nke paraffin waks nke dị elu molecular uka, ya bụ, polymen ogologo nta. N'ihi monomer etlerene kpamkpam, ma si otú a na-arụ ọrụ nke ihe eji arụ ọrụ na-enwe eriri akwara bụ naanị otu. CC Bonst Bark bụ σ nkekọ, nkesa igwe ojii ya na-enwekarị ihe dị obere na carbon na carbon dị obere, ogo nke ntụgharị nke dị obere, nke dị n'ime , na ọnụọgụ nke enwere ike buru ibu.

A na-ejikarị ike Van Dan ike na-eme ihe na-enweghị ike, a na-ejikarị ya dị mma, na cm3 Dị ka roba, naanị na naanị osisi bụ ihe ewezuga, nke bụ nke bụ nke na-agbanwe agbanwe macromolecule.

Pollition polyethylene dị ala (lldpe) na ọnọdụ polymenene dị iche iche, hdpethylene (hdpethylene (hdpe), a ga-enwe nnukwu ihe dị iche iche nke akụkụ dị iche iche, Ma ọnụ ọgụgụ dị nta nke ụdị abụọ dị iche iche, a ka nwere ego Carbonyl na otu Ether na LDPE. Varietiesdị usoro dị iche iche na nha nke alaka ndị dị na ldpe> lldpe> hdpe, alaka nke iguzogide photosegradation na nkewa. HDPe naanị alaka ole na ole, ngalaba nke Macromolecules, a naghị ejikọ ya na nkekọ, dị nro ma na-agbanwe; LDPE bụ ogologo macromolecules likear, nke na-adị m mkpụmkpụ nke na-abawanye na nkọ na-abawanye, macromolecules ndị a na-eme ka ọ dị obere, obere kristal, njupụta, obere kristal. LDPE bụ obere macromolecule nke nwere ogologo ụdọ, a na-eme ka ihe dị ala, na-eme ka ihe dị ala, ọ dịkwa nro, yabụ, ike na okpomoku nke LDPE di ala.

Nhazi nke polyethylene molecule (nhazi geometrical nke atom ma ọ bụ otu ndị na-eme nke kemịkal) Bonst bụ 0.154 nm, akụkụ nke njikọ bụ 109.3 Celsius, na olulu nke ezé bụ 0.253 nm.

Ihe dị iche iche nke polyethylene dị iche iche dị iche, ldpe bụ ihe dị ka 65%, hdpe bụ ihe dị ka 80% ~ 90%, LLDPE bụ ihe dị ka 65% ~ 75%. Site na mmụba nke mkpumkpu, njupụta, nke siri ike, ihe siri ike na ike nke ngwaahịa dị mma, mana mmetụta ya na-emetụta. Polyhethylene iche abụghị naanị kristal dị iche iche, ụdị kristal dị iche iche na paramita kristal abụghị otu.

Ụdị polyethylene gụnyere kristal na obere kristal. A na-enwetakarị mbụ ahụ na-agbaze polyethylene, yae, kristal kristal na-enweta site na uto nke nuclei na-agbasasị n'akụkụ niile; A na - enweta nke ikpeazụ site na mma nke ndọtị nke polyethylene. Tebụl 1-2 na-egosi mkpu iti mkpu nke osisi dị iche iche.

Itutu nke PE na kristal XC, mmekọrịta dị n'etiti ha abụọ bụ:

ebe d bu ihe nlere nke ihe nlere; D1 na D2 bụ oke nke ị na-eji mkpu ike na amorphous pep, n'otu n'otu. N'ozuzu, njupụta nke cripstalline Pusin Pee dị 1.014 g / cm3 na njupụta nke usoro Amorphous bụ 0.84 g / cm3 na 25 ℃.

Nke a dabere na-eburu n'uche na omume nke kristal na polymen nke na-eme klọọkụ (ya bụ, ihe nlele a ga-elele) na-abụkarị ihe atụ nke kristal na usoro amorphous kpamkpam, n'otu n'otu. N'ezie, ọ gaghị ekwe omume na ọ bụla dị 100% kristal ma ọ bụ ihe amorphous kpamkpam.

A na-akọwapụtakarị molular nke polymerization (foto) Ntinye okirikiri nke nkesa (foto) N'ihi usoro polymerization dị iche iche na ọnọdụ arụmọrụ, enwere ike iche na oke mololular dị iche iche, dị ka site na ọtụtụ ihe dị oke mkpa nke 10,000, ọtụtụ narị nde. A na-enwekarị ihe na-ekesa mymersations dị iche iche na ọnọdụ dị iche iche na-agbanwe agbanwe, ọkachasị maka obere nrụgide na-enweghị igwe na-arịa ọrịa Ziegler. A na-ahụkarị Molecular nke nkịtị bụ 400 ~ 120,000, nke Uhmwpe bụ 1,000,000-4,000,000. Ibu elu molecular, ka mma akụrụngwa nke resin, dị ka ike tensihie, nke dị ala, nke dị ala, na-eguzogide nrụgide gburugburu ebe obibi, wdg, mana arụmọrụ na-aka njọ.

Na mgbakwunye na paramita a dị n'elu, enwere ike igosipụta ọnụego nke pedfles site na ọnụego agbaze (mff) na-egosi oke molecular uka, na nke ọzọ, na ala nke mla. Maka LDPE, MFR bụ 20 ~ 50 g / 10 min, maka hdpe 4 ~ 15 min, na maka lldpe 3 ~ 10 g / 10 min.

Maka LDPE, mfr na ọnụ ọgụgụ nkezi nkezi, ihe na-egosi na m nwere mmekọrịta chiri anya na-esochi mmekọrịta dị na:

Ogo nke mla na ntinye ya na-arụ ọrụ dị mkpa na enyemaka dị mkpa na arụmọrụ nke polymer na arụmọrụ na-arụ ọrụ, n'ihi na ọkwa nke mfr bụ anụ ahụ ọnụọgụ nke na-egosipụta ogo viscosity, nke bụ otu ihe na-edozi ahụ, yana enwerekwa mmekọrịta na-esochi n'etiti mfr na ụdị viscosity (η) nke gbazee:

HDPE n'ihi obere mfr, karịa ka ọ dị na viscosity (usoro nke oke molecialar) kwupụtara. A tụrụ ngbasa ozi ụlọ ọrụ na Tetrahydrafthaplene ma ọ bụ des 75 ℃ 75, a na-agbakọ ọnụ ala nke viscosity ya: C.5%, usoro ndị a na-agbakọ agbakọ karịa nza nke viscosity [η ']

ebe η0 bu vivents, pa-s.

Mfr anaghị egosipụta ihe dị na ya, n'ezie nkesa na-arụ ọrụ na-enwe oke mmiri, ebe a na-ahụkarị ihe na-ekesa ihe na-abawanye ụba fọdụ plastizer nke oke molecular. N'ihi na otu nkezi molecular uka, nkesa ndị nwere ike na-akụzi ọfụma. Na mgbakwunye, njupụta PE nwekwara mmetụta dị ukwuu na viscosity nke na-agbaze, obere njupụta, viscosity dịkwa obere. Ya mere, ọnụego agbazekwa mff adịghị mma maka ịtụle oke molecular uka nke penis dị iche iche. Na nkenke, onye ikwu m na-enwekarị obere, nkesa nke LDPE dị mma maka nhazi ya, mana ọtụtụ ihe akụrụngwa na-adịghị mma, yabụ, onye ikwu nke na-arụ ọrụ na ihe ndị ọzọ Osisi ahụ bụ otu okwute ahụ bụ ihe dị mkpa na - emetụta arụmọrụ ikpeazụ nke pe.