Ihe Nlereanya.: TECASINT 4021
Eke: Tecasint
| Ere Ngwa | : | Kilogram |
| Agedị ngwugwu | : | Ngwugwu mbupụ |
The file is encrypted. Please fill in the following information to continue accessing it
Tecasint 4021 Black polymimide na 15% eserese
Bido na isi polymer Tecasint 4011, Tecasint 4021 na-etolite 15% eserese. N'ihi esemokwu dị elu ma yie ihe ngosi, Tecasint 4011 kachasị mma maka ngwa ọgba aghara. Ọ dịkwa mma maka ngwa akọrọ ebe ọ bụ na ihe a na-eme.
Eziokwu
Ngosipụta kemịkal
Pi (pollimide)
Agba
arhacite
Keuju
1.49 g / cm3
Isi atụmatụ
Oke ikuku na-eguzogide
Mmiri dị ala dị ala
Ezigbo slide ma na-eyi ihe
Nnukwu ikuku na ike
Ezigbo Chemical
Na-eguzogide dị elu
Iguzogide megide radieshon dị elu
Na-eche hydrolysis na oke ikuku
Izu ụlọ
Teknụzụ teknụzụ
Teknụzụ iko na-ekpo ọkụ
Mmụta mekanịkal injinịa
P Igwe nri
Industrylọ ọrụ na-arụ ọrụ
Tecasimi 4021 Black Polylidide na mpempe Akwụkwọ Ntanetị Ntanetị
| Mechanical Properties | ||||
| MECHANICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
| Notched impact strength (Charpy) | 3.8 | kJ/m2 | max 7.5 J | DIN EN ISO 179-1 |
| Impact strength (Charpy) | 24.4 | kJ/m2 | max 7.5 J | DIN EN ISO 179-1 |
| Shore hardness | 86 | Shore D | DIN EN ISO 868 | |
| Tensile strength | 93 | MPa | 50 mm/min | DIN EN ISO 527-1 |
| Modulus of elasticity | 4943 | MPa | 1 mm/min | DIN EN ISO 527-1 |
| (tensile test) | ||||
| Flexural strength | 131 | MPa | 10 mm/min | DIN EN ISO 178 |
| Compression strength | 208 | MPa | 10 mm/min | EN ISO 604 |
| Compressive strain at break | 36 | % | 10 mm/min | EN ISO 604 |
| Elongation at break (tensile test) | 3 | % | 50 mm/min | DIN EN ISO 527-1 |
| Modulus of elasticity | 4200 | MPa | 2 mm/min | DIN EN ISO 178 |
| (flexural test) | ||||
| Compression modulus | 2067 | MPa | 1 mm/min | EN ISO 604 |
| Elongation at break (flexural test) | 3.4 | % | 10 mm/min | DIN EN ISO 178 |
| Compression strength | 163 | MPa | 10mm/min, 10% strain | EN ISO 604 |
| Thermal Properties | ||||
| Glass transition temperature | 260 | C | DIN EN ISO 11357 | |
| Thermal expansion (CLTE) | 3.9 - 5.4 | 10-5*1/K | 50-200°C | DIN 53 752 |
| Thermal expansion (CLTE) | 5.3 - 7.3 | 10-5*1/K | 200-300°C | DIN 53 752 |
| Thermal expansion (CLTE) | 7.5 - 10.5 | 10-5*1/K | 300-350°C | DIN 53 752 |
| Other Properties | ||||
| Flammability (UL94) | V0 | - | corresponding to | DIN IEC 60695-11-10; |
| Water absorption | 0.16 | % | 24 h in water, 23°C | DIN EN ISO 62 |
| Water absorption | 0.53 | % | 24 h in water, 80°C | DIN EN ISO 62 |
Nkwupụta nzuzo: Nzuzo gị dị anyị ezigbo mkpa. Companylọ ọrụ anyị na-ekwe nkwa igosipụta ozi nkeonwe gị na mgbasa ozi ọ bụla na-egosi na ọ bụla e ji ikike doo.
Dejupụta ozi ndị ọzọ ka ọ nwee ike ịkpọtụrụ gị ngwa ngwa
Nkwupụta nzuzo: Nzuzo gị dị anyị ezigbo mkpa. Companylọ ọrụ anyị na-ekwe nkwa igosipụta ozi nkeonwe gị na mgbasa ozi ọ bụla na-egosi na ọ bụla e ji ikike doo.
Contact Now