Tecaform Ad Ef eke Pom-H (HOMpopormer Actal)

Tecaform Ad Ef eke Pom-H (HOMpopormer Actal)

Get Latest Price

Ụdị Ụgwọ:	T/T,Paypal
Enweghi ike:	FOB,CFR,CIF,EXW,DDP,DDU
Min. Nhazi:	1 Kilogram
Ụgbọ njem:	Ocean,Land,Air,Express
Port:	Shenzhen,Guangzhou,Hongkong

Kpọtụrụ ugbu a

Nkọwapụta ngwaahịa

Njirimara Ngwaahịa

Nkwakọ ngwaahịa & nzipu

Nkọwapụta ngwaahịa

Njirimara Ngwaahịa

Ihe Nlereanya.: TECAFORM AD EF natural POM-H

Eke: Tecaform

Nkwakọ ngwaahịa & nzipu

Ere Ngwa	:	Kilogram
Agedị ngwugwu	:	Ngwugwu mbupụ

The file is encrypted. Please fill in the following information to continue accessing it

pom delrin Rod mpempe akwụkwọ

CNC POM Akụkụ



Nkọwapụta ngwaahịa

Teca

Tecaform Ad Ef eke bu ihe di nma, na-egosi uzo ozo di iche iche na Pos-H (Hompopopormir Acetal). Ngwongwo a na - agwakọta ọnụ ọgụgụ carbon nwere ihe dị egwu, tinyere njiri mara mma dị egwu, tinyere njiri mara mma dị egwu na iyi oke ike na ike ọgwụgwụ.

Ọzọkwa, tecaforform ad ef eke na-enye nju oyi dịtụ elu, nke siri ike, ma e jiri ya tụnyere Pos-c. Bio actalymer Cecial over na Njirimara mkpuchi mkpuchi eletrik ma dị mfe. N'ihi ya, a biob plasti a dị mma maka ngwa na nnyefe ike dịka gears na ụlọ ọrụ elektrik, ma ọ bụ nhazi nri yana ọtụtụ ọrụ ndị ọzọ.

Dịka onye na-ahụ maka Bio Pommopormer site na Ensinger, Tecaforform Ad eke dị n'ụdị nke achịcha bio Pom-h rods.

Tecaform Ad sest bụ akụkụ nke "a na-eji nlezianya" a na-agụgharị maka echi "

Tecaform Ad Ef Natural Jpg

Eziokwu

Ngosipụta kemịkal

Pom-H (Polyacetal (HOMpomper))

Agba

ucha

Keuju

1.43 g / cm3

Isi atụmatụ

Site na akụrụngwa sitere na ntanetị

ezigbo slide ma na-eyi ihe

ike dị elu

Electring inclitating

Ezigbo Chemical

siri ike isokọ

ezigbo mma

Ọ bụghị mmiri na-ekpo ọkụ na-eguzogide pasent 60 Celsius C

Izu ụlọ

mmụta mekanịkal injinịa

Aircraft na teknụzụ aeropace

elektrọniki

Teknụzụ nri

Industrylọ ọrụ na-arụ ọrụ

Mpempe akwụkwọ teknuzu tecaform ad ef eke nke

Mechanical properties
Mechanical properties	Value	Unit	Parameter	Norm
Modulus of elasticity	3400	MPa	1mm/min	DIN EN ISO 527-2
(tensile test)	3400	MPa	1mm/min	DIN EN ISO 527-2
Tensile strength	79	MPa	50mm/min	DIN EN ISO 527-2
Tensile strength at yield	79	MPa	50mm/min	DIN EN ISO 527-2
Elongation at yield (tensile test)	37	%	50mm/min	DIN EN ISO 527-2
Elongation at break (tensile test)	45	%	50mm/min	DIN EN ISO 527-2
Flexural strength	106	MPa	2mm/min, 10 N	DIN EN ISO 178
Modulus of elasticity	3600	MPa	2mm/min, 10 N	DIN EN ISO 178
(flexural test)	3600	MPa	2mm/min, 10 N	DIN EN ISO 178
Compression modulus	2700	MPa	5mm/min, 10 N	EN ISO 604
Compression strength	19/33/69	MPa	1% / 2% / 5%	EN ISO 604
Impact strength (Charpy)	n.b.	kJ/m2	max. 7,5J	DIN EN ISO 179-1eU
Notched impact strength (Charpy)	15	kJ/m2	max. 7,5J	DIN EN ISO 179-1eA
Shore hardness	85		D	DIN EN ISO 868
Thermal properties
Thermal properties	Value	Unit	Parameter	Norm
Glass transition temperature	-60	C		DIN EN ISO 11357
Melting temperature	182	C		DIN EN ISO 11357
Heat distortion temperature		C	HDT, Method A	ISO-R 75 Method A
Thermal conductivity	0.43	W/(k*m)		ISO 22007-4:2008
Specific heat	1.3	J/(g*K)		ISO 22007-4:2008
Service temperature	150	C	short term	NN
Service temperature	110	C	long term	NN
Thermal expansion (CLTE)	12	10-5*1/K	23-60°C, long.	DIN EN ISO 11359-1;2
Thermal expansion (CLTE)	13	10-5*1/K	23-100°C, long.	DIN EN ISO 11359-1;2
Electrical properties
Electrical properties	Value	Unit	Parameter	Norm
surface resistivity	1014	邃ｦ		-
volume resistivity		O*cm		DIN IEC 60093
Dielectric strength		kV/mm		DIN 53483-1
Other properties
Other properties	Value	Unit	Parameter	Norm
Resistance to hot water/ bases	-			-
Flammability (UL94)	HB		corresponding to	DIN IEC 60695-11-10;
Resistance to weathering	-			-
Water absorption	0.05 / 0.1	%	24h / 96h (23°C)	DIN EN ISO 62
Water absorption		%	saturation (23°C)	DIN EN ISO 62