Ihe Nlereanya.: ULTEM™ PEI PolyEtherImide with 30% Glass reinforced
Eke: Elmm ™
| Ere Ngwa | : | Kilogram |
| Agedị ngwugwu | : | Ngwugwu mbupụ |
The file is encrypted. Please fill in the following information to continue accessing it
Itịpụ ™ 2300 pei bụ ihe exuded 30% na-eme ka polyataiti sikwuo polyatatimide. Ọ bụ polymer na-arụ ọrụ nke nwere oke ọkụ na-enweghị atụ na iguzogide ọkụ. Ọ na-eme nke ọma ruo 340 Celsius F (171 Celsius C), na-eme ka ọ dị mma maka ike / elu ngwa ọkụ, na ndị chọrọ ka ihe ndị na-agbanwe agbanwe na-agbanwe agbanwe na-agbanwe agbanwe. Ọ bụ hydrolysis na-eguzogide ọgwụ, na-eguzogide ọgwụ acidic na ike nke ọtụtụ edozi edozi edozi. Ude ahụ na-enye ihe siri ike ma nwee ike ịkwado ụzọ dị iche iche ka ọ na-enwe ọtụtụ njirimara bara uru nke ngwụcha nke emepela. A na-ejikarị ihe ndị a na-ejikarị emegharị emegharị emegharị emegharị emegharị emegharị, ngwa ọrụ nchịkwa / eletrik, na ọtụtụ ihe eji arụ ọrụ na-achọ ike na ọnọdụ dị elu na ọnọdụ dị elu.
Ude ahụ Ai poi polytatimide (pei) plastic na-acha uhie uhie na-ejikọ ike dị elu na ọnọdụ dị elu na ogologo oge iguzogide. Ude ahụ na-enye ike nkwụsi ike nke ọma na mmiri na-eguzogide. Ude ahụ na-adịkarị ire ọkụ na-eguzogide na iwepụta obere anwụrụ ọkụ. Igwe na-eme ka ọ dịkwuo elu na akụkụ dị ukwuu ma nwee ike ijide onwe gị ma ọ bụrụ na ị nọgide na-enwe ọtụtụ njirimara bara uru nke isi URI. Ihe mgbakwunye iko na-enye ngwaahịa na ike pụrụ iche na-enweghị atụ ma mụbaa. Nke a na klas nke 30% na-eme ka ihe a na-ahụkarị bụ ihe a na-ahụkarị jupụtara na azụ na mpempe akwụkwọ na mkpanaka.
BillM ™ 2300 Pei bipụtara mpempe akwụkwọ 30% na-agbagha
Usoro ntuli aka
Ulm® 1000
Ulm® 2100
Ulm® 2200
Ulm® 2400
Udel® 2300 na-eme ka Polk 1000 na-eme ka ọ na-abawanye ma na-eme ka nkwụsi ike dị iche iche mgbe ị na-enwe ọtụtụ ndị ọka iwu bara uru nke emeghe. Ọzọkwa, ebe ọ bụ ihe nkiri, ọ dị mkpa ka a ga-ewere ya ma ọ bụrụ na cooltant. Ọ bụrụ na e jiri ya mee ihe, a ga-eji akwa nhicha dị arọ iji zere ịchọ ọkụ.
| Specification | Test | Value | Units |
| Specific Gravity, 73°F | D792 | 1.51 | – |
| Tensile Strength @ Yield, 73°F | D638 | 17,000 | psi |
| Tensile Modulus of Elasticity, 73°F | D638 | 800,000 | psi |
| Tensile Elongation (at break), 73°F | D638 | 3 | % |
| Flexural Strength, 73°F | D790 | 27,000 | psi |
| Flexural Modulus of Elasticity | D790 | 850,000 | psi |
| Shear Strength, 73°F | D732 | psi | |
| Compressive Strength – Ultimate | psi | ||
| Compressive Strength at 2% Deformation | D695 | psi | |
| Compressive Strength at 10% Deformation | D695 | 32,000 | psi |
| Deformation Under Load | < 1 | % | |
| Compressive Modulus of Elasticity, 73°F | D695 | 625,000 | |
| Compressive Strength ⊥ to Laminate (Modulus) | psi | ||
| Compressive Strength ⊥ to Laminate (Yield) | psi | ||
| Compressive Strength ⊥ to Laminate (Ultimate) | psi | ||
| Hardness, Durometer (Shore “D” scale) | D2240 | D86 | |
| Hardness, Rockwell (Scale as noted) | D785 | M112 (R127) | Rockwell M |
| Izod Impact, Notched @ 73°F | D256 Type A | 1 | ft.lbs/in. of notch |
| Coefficient of Friction (Dry vs Steel) Static | PTM 55007 | ||
| Coefficient of Friction (Dry vs Steel) Dynamic | PTM 55007 | ||
| Maximum Static Bearing Load (P) | PTM 55007 | 1,000 | psi |
| Maximum Unlubricated No Load Bearing Velocity (V) | PTM 55007 | ft/minute | |
| Maximum Limiting PV (Unlubricated) | PTM 55007 | psi x ft/min. | |
| Wear Factor “K” x 10-10 | PTM 55010 | Cubic in.-min/ft.lbs.hr | |
| Sand Wheel Wear/Abrasion Test | 80 | UHMW=100 | |
| Minimum Mating Surface Hardness | 30 | Rockwell (Brinnell) | |
| Coefficient of Linear Thermal Expansion | E-831 (TMA) | 1.1 | in/in/°F x 10-5 |
| Coefficient of Thermal Expansion // to Laminates | E-831 (TMA) | 1.1 | in/in/°F x 10-5 |
| Coefficient of Thermal Expansion I to Laminates | E-831 (TMA) | 1.1 | in/in/°F x 10-5 |
| Softening Point | 400 | °F | |
| Heat Deflection Temperature 264 psi | D648 | 410 | °F |
| Embrittlement Temperature | °F Min. | ||
| Continuous Service Temperature in Air | 340 | °F Max. | |
| Short Term Service Temperature | 360 | °F Max. | |
| Tg-Glass Transition (Amorphous) | D3418 | 410 | °F |
| Melting Point (Crystalline) Peak | D3418 | °F | |
| Thermal Conductivity | F433 | 1.56 | BTU-in/(hr/ft2°F) |
| Dielectric Strength Short Term | D149 | 770 | Volts/mil |
| Surface Resistivity | D257 | >1013 | ohm/cm |
| Volume Resistivity | D257 | ohm/cm | |
| Dielectric Constant, 106 Hz | D150 | 3.7 | |
| Dissipation Factor, 106 Hz | D150 | 0.0015 | |
| Flammability @ 3.1mm(1/8 in.) UL94 | UL94 | V-0 | |
| Arc Resistance | seconds | ||
| Water Absorption, Immersion 24 Hours | D570 (2) | 0.18 | % |
| Water Absorption, Immersion Saturation | D570 (2) | .9 | % |
| Machinability Rating | 1 | 1=easy, 10=difficult | |
| Rod Diameter Availability (Off the Shelf) | .50 | 6.0 | inches |
| Sheet Thickness Availability (Off the Shelf) | .030 | 3.0 | inches |
| Characteristics / Attributes | Superior Chemical Resistance / 340F Cont. Service Temp Excellent rigidity and stiffness. |
Nkwupụta nzuzo: Nzuzo gị dị anyị ezigbo mkpa. Companylọ ọrụ anyị na-ekwe nkwa igosipụta ozi nkeonwe gị na mgbasa ozi ọ bụla na-egosi na ọ bụla e ji ikike doo.
Dejupụta ozi ndị ọzọ ka ọ nwee ike ịkpọtụrụ gị ngwa ngwa
Nkwupụta nzuzo: Nzuzo gị dị anyị ezigbo mkpa. Companylọ ọrụ anyị na-ekwe nkwa igosipụta ozi nkeonwe gị na mgbasa ozi ọ bụla na-egosi na ọ bụla e ji ikike doo.
Contact Now